Low loss EELS and EFTEM study of Bi 2Te 3 based bulk and nanomaterials

Link:
Autor/in:
Erscheinungsjahr:
2011
Medientyp:
Text
Schlagworte:
  • Thermoelectricity
  • Thermoelectric equipment
  • Bismuth telluride
  • Thermoelectric Equipment
  • Thermal Conductivity
  • Thermoelectricity
  • Thermoelectric equipment
  • Bismuth telluride
  • Thermoelectric Equipment
  • Thermal Conductivity
Beschreibung:
  • Energy-filtered transmission electron microscopy (EFTEM) yields new possibilities for the investigation of Bi 2Te 3 based nanomaterials. Combined low-loss electron energy-loss spectroscopy (EELS) and energy-dispersive x-ray microanalysis (EDS) and energy-filtered TEM were applied on a Zeiss 912Ω TEM to investigate nanowires, thin films, and bulk materials. Multilayered Bi-Sb-Te nanowires with a diameter of 65 nm and a period of 200 nm and stoichiometric Bi 2Te 3 nanowires were grown by potential-pulsed electrochemical deposition. Tellurium elemental maps of the multilayered nanowires were obtained by two-window edge-jump ratio images (EJI). EDS chemical analysis showed that small Te fluctuations of 3 at.% yielded significant contrast in EJI. Energy-filtered TEM applied on nano-alloyed Bi 2Te 3 thin films grown by molecular beam epitaxy (MBE) revealed 10-20 nm thick Bi-rich blocking layers at grain boundaries. Plasmon spectroscopy by EELS was applied on Bi 2(Te 0.91Se 0.09) 3 bulk and yielded a plasmon energy of 16.9 eV. Finally, plasmon dispersion was measured for Bi 2(Te 0.91Se 0.09) 3bulk by angle-resolved EELS, which yields a fingerprint of the anisotropy and the dimensionality of the electronic structure of the materials. © 2011 Materials Research Society.
Lizenz:
  • info:eu-repo/semantics/restrictedAccess
Quellsystem:
Forschungsinformationssystem der UHH
Interne Metadaten
Quelldatensatz
oai:www.edit.fis.uni-hamburg.de:publications/5a4d60c4-cde8-4b2f-a431-1af65fbb6827