Surface Characteristics of Esthetic Nickel⁻Titanium and Beta-Titanium Orthodontic Archwires Produced by Plasma Electrolytic Oxidation (PEO)-Primary Results
- Link:
- Autor/in:
- Erscheinungsjahr:
- 2019
- Medientyp:
- Text
- Beschreibung:
-
BACKGROUND/AIM: There is continuing interest in engineering esthetic labial archwires. The aim of this study was to coat nickel-titanium (NiTi) and beta-titanium (β-Ti), also known as titanium molybdenum (TMA), archwires by plasma electrolytic oxidation (PEO) and to analyze the characteristics of the PEO-surfaces.
MATERIALS AND METHODS: PEO-coatings were generated on 0.014-inch NiTi and 0.19 × 0.25-inch β-Ti archwires. The surfaces were analyzed by scanning electron microscopy and stereomicroscopy. Cytocompatibility testing was performed with ceramized and untreated samples according to EN ISO 10993-5 in XTT-, BrdU- and LDH-assays. The direct cell impact was analyzed using LIVE-/DEAD-staining. In addition, the archwires were inserted in an orthodontic model and photographs were taken before and after insertion.
RESULTS: The PEO coatings were 15 to 20 µm thick with a whitish appearance. The cytocompatibility analysis revealed good cytocompatibility results for both ceramized NiTi and β-Ti archwires. In the direct cell tests, the ceramized samples showed improved compatibility as compared to those of uncoated samples. However, bending of the archwires resulted in loss of the PEO-surfaces. Nevertheless, it was possible to insert the β-Ti PEO-coated archwire in an orthodontic model without loss of the PEO-ceramic.
CONCLUSION: PEO is a promising technique for the generation of esthetic orthodontic archwires. Since the PEO-coating does not resist bending, its clinical use seems to be limited so far to orthodontic techniques using straight or pre-bent archwires.
- Lizenz:
-
- info:eu-repo/semantics/openAccess
- Quellsystem:
- Forschungsinformationssystem des UKE
Interne Metadaten
- Quelldatensatz
- oai:pure.atira.dk:publications/9dd1b2cc-ed79-4521-adcd-8b5334e18010